Synthetic Fiber Reinforced Concrete in Marine Environments and Indirect Tension Test
Title
Synthetic Fiber Reinforced Concrete in Marine Environments and Indirect Tension Test.
Creator
Flaherty, Ryan, Presuel-Moreno, Francisco, Florida Atlantic University, College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering
Abstract/Description
An experiment was conducted to evaluate the durability, toughness, and strength of Synthetic Fiber Reinforced Concrete after being immersed in five separate environments for one year at FAU SeaTech. The specimens were molded and reinforced with two-inch Polypropylene/Polyethylene Fibers in a concrete aggregate matrix and were cut into identical sizes. Some of these environments had accelerated parameters meant to increase degradation to simulate longevity and imitate harsh environments or...
Show moreAn experiment was conducted to evaluate the durability, toughness, and strength of Synthetic Fiber Reinforced Concrete after being immersed in five separate environments for one year at FAU SeaTech. The specimens were molded and reinforced with two-inch Polypropylene/Polyethylene Fibers in a concrete aggregate matrix and were cut into identical sizes. Some of these environments had accelerated parameters meant to increase degradation to simulate longevity and imitate harsh environments or seawater conditions. The environments consisted of: a high humidity locker (ideal conditions), submerged in the Intracoastal Waterway (FAU barge), seawater immersion, a wet and dry seawater immersion simulating a splash/tidal zone, and another in low pH seawater. The latter three were in an elevated temperature room (87-95°F) which produced more degradative properties. The specimens were monitored and the environments were controlled. The specimens were then evaluated using the IDT test method using force to initiate first-cracking and post-cracking behaviors.
Show less
Date Issued
2018
PURL
http://purl.flvc.org/fau/fd/FA00013029
Subject Headings
Reinforced concrete, Fiber-reinforced concrete--Testing, Synthetic fibers
Format
Document (PDF)
Investigation of nanoscale reinforcement into textile polymers
Title
Investigation of nanoscale reinforcement into textile polymers.
Creator
Khan, Mujibur Rahman., College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering
Abstract/Description
A dual inclusion strategy for textile polymers has been investigated to increase elastic energy storage capacity of fibers used in high velocity impact applications. Commercial fibers such as Spectra and Dyneema are made from ultra high molecular weight polyethylene (UHMWPE). Dynamic elastic energy of these fibers is still low therefore limiting their wholesale application without a secondary metallic or ceramic component. The idea in this investigation is to develop methodologies so that the...
Show moreA dual inclusion strategy for textile polymers has been investigated to increase elastic energy storage capacity of fibers used in high velocity impact applications. Commercial fibers such as Spectra and Dyneema are made from ultra high molecular weight polyethylene (UHMWPE). Dynamic elastic energy of these fibers is still low therefore limiting their wholesale application without a secondary metallic or ceramic component. The idea in this investigation is to develop methodologies so that the elastic energy of polyethylene based fibers can be increased by several folds. This would allow manufacturing of an all-fabric system for high impact applications. The dual inclusion consists of a polymer phase and a nanoscale inorganic phase to polyethylene. The polymer phase was nylon-6 and the inorganic phase was carbon nanotubes (CNTs). Nylon-6 was blended as a minor phase into UHMWPE and was chosen because of its large fracture strain - almost one order higher than that of UHMWPE. On the other hand, CNTs with their very high strength, modulus, and aspect ratio, contributed to sharing of load and sliding of polymer interfaces as they aligned during extrusion and strain hardening processes. A solution spinning process was developed to produce UHMWPE filaments reinforced with CNTs and nylon-6. The procedure involved dispersing of CNTs into paraffin oil through sonication followed by dissolving polymers into paraffin-CNT solution using a homogenizer. The admixture was fed into a single screw extruder for melt mixing and extrusion through an orifice. The extrudate was rinsed via a hexane bath, stabilized through a heater, and then drawn into a filament winder with controlled stretching. In the next step, the as produced filaments were strain-hardened through repeated loading unloading cycles under tension., Neat and reinforced filaments were characterized through DSC (Differential Scanning Calorimetry), XRD (X-ray Diffraction), Raman Spectroscopy, SEM (Scanning Electron Microscope), and mechanical tests. Phenomenal improvement in properties was found; modulus, strength, fracture strain, and elastic energy increased by 219%, 100%, 107% and 88%, respectively before strain hardening. Once strain hardened the strength, modulus and elastic energy increased by almost one order of magnitude. Source of these improvements were traced to increase in crystallinity and rate of crystallization, formation of microdroplets as a minor phase, sliding between minor and major phases, coating of nanotubes with polymer and alignment of nanotubes.
Show less
Date Issued
2010
PURL
http://purl.flvc.org/FAU/2976443
Subject Headings
Nanostructured materials, Composite materials, Textile fibers, Synthetic, Polymers, Electric properties