Current Search: Marine steel--Fatigue (x)
-
-
Title
-
Effect of cathodic protection and cyclic frequency on corrosion fatigue of selected high strength steels in seawater.
-
Creator
-
Badve, Ashwin P., Florida Atlantic University, Hartt, William H.
-
Abstract/Description
-
Study of selected candidate steels for offshore application was undertaken to observe the effects of cathodic protection and cyclic frequency on corrosion fatigue life. Keyhole Compact Tension Fatigue experiments under constant amplitude sinusoidal loading and stress ratio of 0.5 were performed on 25.4 mm thick specimens in natural sea water and also in air upon three different steels (Y.S. 500-563 MPa). These steels represented different strengthening techniques, namely precipitation...
Show moreStudy of selected candidate steels for offshore application was undertaken to observe the effects of cathodic protection and cyclic frequency on corrosion fatigue life. Keyhole Compact Tension Fatigue experiments under constant amplitude sinusoidal loading and stress ratio of 0.5 were performed on 25.4 mm thick specimens in natural sea water and also in air upon three different steels (Y.S. 500-563 MPa). These steels represented different strengthening techniques, namely precipitation hardening, direct quenching--a thermomechanical control process (TMCP), and controlled rolling. Cathodic polarization was in the range between freely corroding and -1.10 Volts (SCE). The tests were performed at a frequency of 0.3 and 1.0 Hz. The results are presented in the S-N and potential versus cycles to initiation format. No effect of frequency (1.0-0.3 Hz) was observed at cathodic protection of -1.10 V (SCE). The steels showed an increase in fatigue life to an optimum potential, and excessive potentials were detrimental. The fatigue life in dry air was greater than in laboratory air (~50% RH).
Show less
-
Date Issued
-
1989
-
PURL
-
http://purl.flvc.org/fcla/dt/14494
-
Subject Headings
-
Marine steel--Fatigue, Offshore structures, Sea-water corrosion, Corrosion and anti-corrosives
-
Format
-
Document (PDF)