Determination of the tensile strength of the fiber/matrix interface for glass/epoxy & carbon/vinylester.
-
Creator
-
Totten, Kyle, Carlsson, Leif A., Florida Atlantic University, College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering
-
Abstract/Description
-
The tensile strength of the fiber/matrix interface was determined through the development of an innovativetest procedure.Aminiature tensile coupon with a through-thickness oriented, embedded single fiberwas designed. Tensile testing was conducted ina scanning electron microscope (SEM)while the failure process could be observed.Finite element stress analysis was conducted to determine the state of stressat the fiber/matrix interface in the tensile loaded specimen, and the strength of the...
Show moreThe tensile strength of the fiber/matrix interface was determined through the development of an innovativetest procedure.Aminiature tensile coupon with a through-thickness oriented, embedded single fiberwas designed. Tensile testing was conducted ina scanning electron microscope (SEM)while the failure process could be observed.Finite element stress analysis was conducted to determine the state of stressat the fiber/matrix interface in the tensile loaded specimen, and the strength of the interface.Test specimensconsistingof dry E-glass/epoxy and dry and seawater saturatedcarbon/vinylester510Awere preparedand tested.The load at the onset of debondingwascombined withthe radial stressdistributionnear thefree surface of the specimento reducethe interfacial tensile strength. For glass/epoxy, was 36.7±8.8MPa.For the dryand seawater saturated carbon/vinylester specimensthetensilestrengthsof the interface were 23.0±6.6 and 25.2±4.1MPa, respectively.The difference is not significant.
Show less
-
Date Issued
-
2015
-
PURL
-
http://purl.flvc.org/fau/fd/FA00004415, http://purl.flvc.org/fau/fd/FA00004415
-
Subject Headings
-
Composite materials -- Mechanical properties, Composite materials -- Testing, Fibrous composites -- Mechanical properties, Polymeric composites -- Mechanical properties, Viscoelasticity
-