APPLICABILITY OF CATHODIC PROTECTION IN PREVENTION OF CORROSION DAMAGE TO STEEL TENDONS IN PRESTRESSED CONCRETE (HIGH STRENGTH STEEL, HYDROGEN EMBRITTLEMENT, BRITTLE CRACKING).
-
Creator
-
SCANNELL, WILLIAM THOMAS., Florida Atlantic University, Hartt, William H., College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering
-
Abstract/Description
-
A series of experiments were performed on a single tendon in a prestressed concrete slab for the purpose of studying the susceptibility of the high strength steel to brittle fracture as a result of cathodic protection. The procedure first involved impressing an anodic current until active potentials were recorded along the tendon length. Subsequently, cathodic polarization of the midsection of the tendon to -1.3 V(SCE) was effected. After a prescribed time, the tendon was removed and...
Show moreA series of experiments were performed on a single tendon in a prestressed concrete slab for the purpose of studying the susceptibility of the high strength steel to brittle fracture as a result of cathodic protection. The procedure first involved impressing an anodic current until active potentials were recorded along the tendon length. Subsequently, cathodic polarization of the midsection of the tendon to -1.3 V(SCE) was effected. After a prescribed time, the tendon was removed and sectioned into 15 ern lengths. Each segment strand was then notched and strained to failure, in three-point bending, in order to determine any effect of cathodic protection on the mechanical properties of the material. Differences in average failure loads were compared to determine if a loss of load-bearing capacity and brittle fracture occurred due to hydrogen absorption.
Show less
-