Influence of chlorides and surface condition on pitting potential of high performance reinforcing steel

Download pdf | Full Screen View

Date Issued:
2004
Summary:
In order to identify the influence of chlorides and surface finish on pitting potential of high performance reinforcing steel, cyclic polarization scans were performed on types 304, 2201 and 3Cr12 stainless steels and MMFX-II in simulated pore solution to which chloride was incrementally added. Furthermore, the surface condition was investigated with regard to the pitting potential. Pitting potential distributions versus the chloride content and surface finish were obtained. Pitting resistance was lowered as chloride was added and as the surface became rougher. Furthermore, a critical chloride to hydroxide ratio as a function of potential was determined for each material. Finally, according to the results of this study, the MMFX reinforcing steel was considered to have a corrosion performance close to that of Type 2201 stainless steel for bridge use. MMFX-II specimens with a polished surface exhibited more positive pitting potentials than did ones with an as-received finish.
Title: Influence of chlorides and surface condition on pitting potential of high performance reinforcing steel.
77 views
26 downloads
Name(s): Leroux, Virginie Edwige.
Florida Atlantic University, Degree grantor
Hartt, William H., Thesis advisor
College of Engineering and Computer Science
Department of Ocean and Mechanical Engineering
Type of Resource: text
Genre: Electronic Thesis Or Dissertation
Issuance: monographic
Date Issued: 2004
Publisher: Florida Atlantic University
Place of Publication: Boca Raton, Fla.
Physical Form: application/pdf
Extent: 108 p.
Language(s): English
Summary: In order to identify the influence of chlorides and surface finish on pitting potential of high performance reinforcing steel, cyclic polarization scans were performed on types 304, 2201 and 3Cr12 stainless steels and MMFX-II in simulated pore solution to which chloride was incrementally added. Furthermore, the surface condition was investigated with regard to the pitting potential. Pitting potential distributions versus the chloride content and surface finish were obtained. Pitting resistance was lowered as chloride was added and as the surface became rougher. Furthermore, a critical chloride to hydroxide ratio as a function of potential was determined for each material. Finally, according to the results of this study, the MMFX reinforcing steel was considered to have a corrosion performance close to that of Type 2201 stainless steel for bridge use. MMFX-II specimens with a polished surface exhibited more positive pitting potentials than did ones with an as-received finish.
Identifier: 9780496233526 (isbn), 13103 (digitool), FADT13103 (IID), fau:9967 (fedora)
Collection: FAU Electronic Theses and Dissertations Collection
Note(s): College of Engineering and Computer Science
Thesis (M.S.)--Florida Atlantic University, 2004.
Subject(s): Reinforcing bars--Corrosion
Steel, Structural--Corrosion
Chlorides
Held by: Florida Atlantic University Libraries
Persistent Link to This Record: http://purl.flvc.org/fcla/dt/13103
Sublocation: Digital Library
Use and Reproduction: Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder.
Use and Reproduction: http://rightsstatements.org/vocab/InC/1.0/
Host Institution: FAU
Is Part of Series: Florida Atlantic University Digital Library Collections.