Improving the Mechanical Properties of Nano-Hydroxyapatite
| Title: | Improving the Mechanical Properties of Nano-Hydroxyapatite. |
 156 views 67 downloads |
|---|---|---|
| Name(s): |
Khanal, Suraj P., author Leventouri, Theodora, Thesis advisor Florida Atlantic University, Degree grantor Charles E. Schmidt College of Science Department of Physics |
|
| Type of Resource: | text | |
| Genre: | Electronic Thesis Or Dissertation | |
| Date Created: | 2016 | |
| Date Issued: | 2016 | |
| Publisher: | Florida Atlantic University | |
| Place of Publication: | Boca Raton, Fla. | |
| Physical Form: | application/pdf | |
| Extent: | 119 p. | |
| Language(s): | English | |
| Summary: | Hydroxyapatite (HAp) is an ideal bioactive material that is used in orthopedics. Chemical composition and crystal structure properties of HAp are similar to the natural bone hence it promotes bone growth. However, its mechanical properties of synthetic HAp are not sufficient for major load-bearing bone replacement. The potential of improving the mechanical properties of synthetic hydroxyapatite (HAp) by incorporating carboxyl functionalized single walled carbon nanotubes (CfSWCNT) and polymerized ɛ-caprolactam (nylon) is studied. The fracture toughness, tensile strength, Young’s modulus, stiffness and fracture energy were studied for a series of HAp samples with CfSWCNT concentrations varying from 0 to 1.5 wt. % without, and with nylon addition. X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Transmission Electron Microscopy (TEM) and Differential Scanning Calorimetry (DSC) were used to characterize the samples. The fracture toughness and tensile test was performed under the standard protocol of ASTM D5045 and ASTM D638-02a respectively. Reproducible maximum values of (3.60 ± 0.3) MPa.m1/2 for fracture toughness and 65.38 MPa for tensile strength were measured for samples containing 1 wt. % CfSWCNT and nylon. The Young’s modulus, stiffness and fracture energy of the samples are 10.65 GPa, 1482.12 N/mm, and 644 J/m2 respectively. These values are comparable to those of the cortical bone. Further increase of the CfSWCNT content results to a decreased fracture toughness and tensile strength and formation of a secondary phase. | |
| Identifier: | FA00004675 (IID) | |
| Degree granted: | Dissertation (Ph.D.)--Florida Atlantic University, 2016. | |
| Collection: | FAU Electronic Theses and Dissertations Collection | |
| Note(s): | Includes bibliography. | |
| Subject(s): |
Biomedical engineering -- Materials Biomedical materials -- Mechanical properties Nanostructured materials -- Mechanical properties |
|
| Held by: | Florida Atlantic University Libraries | |
| Sublocation: | Digital Library | |
| Links: | http://purl.flvc.org/fau/fd/FA00004675 | |
| Persistent Link to This Record: | http://purl.flvc.org/fau/fd/FA00004675 | |
| Use and Reproduction: | Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder. | |
| Use and Reproduction: | http://rightsstatements.org/vocab/InC/1.0/ | |
| Host Institution: | FAU | |
| Is Part of Series: | Florida Atlantic University Digital Library Collections. |