Evaluation of corrosion behavior of ion vapor deposited aluminum related coating systems

Download pdf | Full Screen View

Date Issued:
1993
Summary:
Experiments were conducted to investigate the effectiveness of ion vapor deposited (IVD) aluminum as a base coat for polyurethane topcoat systems in marine environments. Three test environments were used including marine atmospheric atmosphere, quiescent filtered seawater open to laboratory air and aerated seawater. Visual observation and electrochemical impedance spectroscopy techniques were primary testing methods; other characterizations included adhesion tape test, coating thickness measurements, holiday detection, optical microscopy, open circuit potential measurements and potentiodynamic polarization. It was found that IVD aluminum was a good candidate for replacement of environmentally sensitive coatings on AA2219-T87 and AISI 4340 steel substrates, respectively. The IVD aluminum coating provided good sacrificial protection and served as a good base for polyurethane topcoat systems. Electrochemical impedance spectroscopy was a suitable method to predict coating performance in the early stages of exposure.
Title: Evaluation of corrosion behavior of ion vapor deposited aluminum related coating systems.
82 views
24 downloads
Name(s): Hang, Ling.
Florida Atlantic University, Degree grantor
McIntyre, Jack F., Thesis advisor
Type of Resource: text
Genre: Electronic Thesis Or Dissertation
Issuance: monographic
Date Issued: 1993
Publisher: Florida Atlantic University
Place of Publication: Boca Raton, Fla.
Physical Form: application/pdf
Extent: 157 p.
Language(s): English
Summary: Experiments were conducted to investigate the effectiveness of ion vapor deposited (IVD) aluminum as a base coat for polyurethane topcoat systems in marine environments. Three test environments were used including marine atmospheric atmosphere, quiescent filtered seawater open to laboratory air and aerated seawater. Visual observation and electrochemical impedance spectroscopy techniques were primary testing methods; other characterizations included adhesion tape test, coating thickness measurements, holiday detection, optical microscopy, open circuit potential measurements and potentiodynamic polarization. It was found that IVD aluminum was a good candidate for replacement of environmentally sensitive coatings on AA2219-T87 and AISI 4340 steel substrates, respectively. The IVD aluminum coating provided good sacrificial protection and served as a good base for polyurethane topcoat systems. Electrochemical impedance spectroscopy was a suitable method to predict coating performance in the early stages of exposure.
Identifier: 14970 (digitool), FADT14970 (IID), fau:11749 (fedora)
Collection: FAU Electronic Theses and Dissertations Collection
Note(s): College of Engineering and Computer Science
Thesis (M.S.)--Florida Atlantic University, 1993.
Subject(s): Aluminum coating
Corrosion and anti-corrosives
Metals--Corrosion fatigue
Electrochemical analysis
Held by: Florida Atlantic University Libraries
Persistent Link to This Record: http://purl.flvc.org/fcla/dt/14970
Sublocation: Digital Library
Use and Reproduction: Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder.
Use and Reproduction: http://rightsstatements.org/vocab/InC/1.0/
Host Institution: FAU
Is Part of Series: Florida Atlantic University Digital Library Collections.