FATIGUE CRACK DEVELOPMENT IN CATHODICALLY POLARIZED WELDED STEEL IN SEAWATER

Download pdf | Full Screen View

Date Issued:
1981
Summary:
The fatigue crack growth behavior of welded ABS DH32 steel spec~mens cathodically polarized to -1.00 volt (Cu-CuS04) and subjected to bending fatigue of nominal stress + 69 MN/m^2 (+- 10 ksi) in seawater was investigated. Small non-propagating surface cracks with lengths up to 4.93 mm formed in the specimens. There were no s~gns of failure after 36 x 10^6 cycles when the experiment was terminated. Comparison of this test with similar freely corroding and -0.85 volt (Cu-CuS04) tests indicated that -1.00 volt (Cu-CuS04) cathodic protection is conducive to arrestment of small fatigue cracks. This suggests that modest cathodic over-protection of steel in seawater may beneficial.
Title: FATIGUE CRACK DEVELOPMENT IN CATHODICALLY POLARIZED WELDED STEEL IN SEAWATER.
67 views
21 downloads
Name(s): WEHLING, CHRISTOPHER MARK.
Florida Atlantic University, Degree grantor
Hartt, William H., Thesis advisor
College of Engineering and Computer Science
Department of Ocean and Mechanical Engineering
Type of Resource: text
Genre: Electronic Thesis Or Dissertation
Issuance: monographic
Date Issued: 1981
Publisher: Florida Atlantic University
Place of Publication: Boca Raton, Fla.
Physical Form: application/pdf
Extent: 36 p.
Language(s): English
Summary: The fatigue crack growth behavior of welded ABS DH32 steel spec~mens cathodically polarized to -1.00 volt (Cu-CuS04) and subjected to bending fatigue of nominal stress + 69 MN/m^2 (+- 10 ksi) in seawater was investigated. Small non-propagating surface cracks with lengths up to 4.93 mm formed in the specimens. There were no s~gns of failure after 36 x 10^6 cycles when the experiment was terminated. Comparison of this test with similar freely corroding and -0.85 volt (Cu-CuS04) tests indicated that -1.00 volt (Cu-CuS04) cathodic protection is conducive to arrestment of small fatigue cracks. This suggests that modest cathodic over-protection of steel in seawater may beneficial.
Identifier: 14091 (digitool), FADT14091 (IID), fau:10905 (fedora)
Collection: FAU Electronic Theses and Dissertations Collection
Note(s): College of Engineering and Computer Science
Thesis (M.S.)--Florida Atlantic University, 1981.
Subject(s): Steel--Fatigue
Held by: Florida Atlantic University Libraries
Persistent Link to This Record: http://purl.flvc.org/fcla/dt/14091
Sublocation: Digital Library
Use and Reproduction: Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder.
Use and Reproduction: http://rightsstatements.org/vocab/InC/1.0/
Host Institution: FAU
Is Part of Series: Florida Atlantic University Digital Library Collections.