Raman spectroscopic studies of stabilized zirconia at elevated temperatures.
-
Creator
-
Lacher, Nathan, Florida Atlantic University, Liu, David, Charles E. Schmidt College of Science, Department of Physics
-
Abstract/Description
-
Raman spectroscopy was used to determine the phase structure and phase stability of zirconia mixtures for various elevated temperatures, type and concentration of oxides added to zirconia, and fabrication process. All 8 wt.% yttria samples showed mostly the tetragonal structure at room temperature. Three of the four 8 wt.% yttria samples exhibited the tetragonal structure at elevated temperatures, while no conclusion was inferred for the powdered sample. As compared with yttria, ceria is a...
Show moreRaman spectroscopy was used to determine the phase structure and phase stability of zirconia mixtures for various elevated temperatures, type and concentration of oxides added to zirconia, and fabrication process. All 8 wt.% yttria samples showed mostly the tetragonal structure at room temperature. Three of the four 8 wt.% yttria samples exhibited the tetragonal structure at elevated temperatures, while no conclusion was inferred for the powdered sample. As compared with yttria, ceria is a less effective stabilizer with respect to the zirconia tetragonal structure. A monoclinic transformation between 400 K and 800 K was observed in the 4 wt.% yttria sample which had been processed by rapid quenching. Adding alumina to 4 wt.% yttria did not completely stabilize the tetragonal structure at or above room temperature, making it a less effective stabilizer than yttria or ceria. The phase transformation was responsible for the unusual values in the Gr uneisen parameters obtained for the 4 wt.% yttria sample.
Show less
-
Date Issued
-
1990
-
PURL
-
http://purl.flvc.org/fcla/dt/14589
-
Subject Headings
-
Zirconium oxide--Spectra, Raman spectroscopy
-
Format
-
Document (PDF)