- Durability prediction of recycled aggregate concrete under accelerated aging and environmental exposure.
- Creator
- Gonzalez, Lillian, College of Engineering and Computer Science, Department of Civil, Environmental and Geomatics Engineering
- Abstract/Description
-
This study is to compare the performance of recycled aggregate concrete and the impact of up to 50% cement replacement with fly ash on durability. Water content, sieve analysis, standard and modified compaction tests were performed to assess the physical properties of the recycled aggregate concrete. Accelerated aging tests were performed to predict the long term durability of the recycled aggregate concrete. Following Arrhenius modeling and TTS and SIM accelerated aging protocols, a time...
Show moreThis study is to compare the performance of recycled aggregate concrete and the impact of up to 50% cement replacement with fly ash on durability. Water content, sieve analysis, standard and modified compaction tests were performed to assess the physical properties of the recycled aggregate concrete. Accelerated aging tests were performed to predict the long term durability of the recycled aggregate concrete. Following Arrhenius modeling and TTS and SIM accelerated aging protocols, a time versus stiffness master curve was created. This allowed the prediction of equivalent age using experimental data and theoretical analysis. To account for environmental exposure, the specimens underwent 24 and 48 hours of wet-dry cycling and subjected. Overall there was an increase in stiffness and strength from the specimens containing fly ash. All tests performed predicted equivalent age beyond the testing period of 144 hrs. and up to 7 years. Specimens containing fly maintained a constant and higher density to environmental exposure.
Show less - Date Issued
- 2010
- PURL
- http://purl.flvc.org/FAU/3353087
- Subject Headings
- Concrete, Mechanical properties, Testing, Concrete, Environmental aspects, Sustainable construction, High strength concrete, Testing, Cement composites, Testing
- Format
- Document (PDF)
- Title
- Durability of a recycled aggregate concrete base course material under coupled environmental exposure and cyclic.
- Creator
- Gonzalez, Lillian, Sobhan, Khaled, Florida Atlantic University, College of Engineering and Computer Science, Department of Civil, Environmental and Geomatics Engineering
- Abstract/Description
-
Long term durability is a major concern for wide-scale use of recycled aggregate materials in civil engineering construction. The purpose of this study is to provide an insight into the damaging effects of combined wet-dry cycles and repeated mechanical loading in a recycled aggregate concrete (RAC) base course material made from recycled crushed concrete aggregate and cement. A coordinated experimental program followed by a mechanistic pavement modeling and life cycle analysis was conducted...
Show moreLong term durability is a major concern for wide-scale use of recycled aggregate materials in civil engineering construction. The purpose of this study is to provide an insight into the damaging effects of combined wet-dry cycles and repeated mechanical loading in a recycled aggregate concrete (RAC) base course material made from recycled crushed concrete aggregate and cement. A coordinated experimental program followed by a mechanistic pavement modeling and life cycle analysis was conducted as part of this research study. This laboratory investigation was divided into three phases each consisting of both wet-dry exposed specimens (WD), and control or non wet-dry exposed specimens (NWD). Phase I experiments involved monotonic loading tests under compression and flexure to evaluate the strength properties. Phase II involved testing a total of 108 cylindrical specimens in cyclic compressive loading at three different stress ratios. After each regime of cyclic loading, residual compressive strengths were determined. In addition, the load-deformation hysteresis loops and the accumulated plastic deformation were continuously monitored through all loading cycles. Phase III included a flexural fatigue test program on 39 beam specimens, and fracture testing program on 6 notched beam specimens, each one having 19-mm initial notch. Traditional SR-N curves, relating the Stress Ratio (SR) with the number of cycles to failure (N or Nf), were developed. Fatigue crack growth rate and changes in Stress Intensity Factors were obtained to determine Paris Law constants and fracture toughness. A mechanistic analysis of a typical highway pavement incorporating RAC base was performed with KENPAVE program, followed by a Life Cycle Analysis (LCA) using the GaBi software. It was found that the specimens subjected to wet-dry cycles suffered significantly higher damage expressed in terms of accumulated plastic deformation, and loss of residual compressive strength, modulus, fatigue endurance limit, and design life, compared to specimens not exposed to wet-dry cycles. Although such degradation in material properties are important considerations in pavement design, a concurrent Life Cycle Analysis demonstrated that recycled aggregate concrete base course still holds promise as an alternative construction material from environmental stand point.
Show less - Date Issued
- 2014
- PURL
- http://purl.flvc.org/fau/fd/FA00004116, http://purl.flvc.org/fau/fd/FA00004116
- Subject Headings
- Aggregates (Building materials ) -- Recycling, Concrete -- Mechanical properties, Construction and demolition debris -- Recycling, Structural engineering, Sustainable construction, Waste products as road materials